Induction Hardened Steel Piston Rod for Hydraulic Cylinder
Hard chrome piston rods processed by more than ten processing, made by steel bar in material CK45, 20MnV6, 42CrMo4, SUS304, SUS316 etc.. Dia. Precision level of f7 tolerance, surface hardness min. HV900.
Chrome layer thickness 20-50micron can be choice, Salt spray test 60-90hours.
Induction hardened hardness HRC55±2, hardened depth 0.5-3.5mm can be choice.
>Equipment cover all production processing with stick QC system make better quality and keep improve.
>Huge material purchasing reduce production cost and final rate.
>Rich stock for normal size, order could be fast delivery in 7days.
>100% inspection and one-year quality guarantee to avoid any risk choice us.
CK45 Hard Chrome Rod
| Steel Grade | C45E (EN 10083) |
| Tolerance | ISO f7 |
| Length | 4000mm, 5800mm, 6000mm, 7500mm can be choice |
| Roughness | max. Ra0.20µm (statistic average: 0.05 - 0.15µm) |
| Hardness | HRC 15-25, HRC 20-30 (Based on different heat treatment) |
| Chrome Thickness | 20-50µm can be choice |
| Chrome Hardness | min. 900 HV (0.1) |
| Straightness | <=Ø16 mm: max. 0.3 mm : 1000 mm > Ø16 mm: max. 0.2 mm : 1000 mm |
| Mechanical Properties | According to EN 10083-2 |
CK45 Induction Hardened Chrome Rod
| Steel Grade | C45E (EN 10083) |
| Tolerance | ISO f7 |
| Length | 4000mm, 5800mm, 6000mm, 7500mm can be choice |
| Roughness | max. Ra0.20µm (statistic average: 0.05 - 0.15µm) |
| Hardness | HRC 55+/-2 |
| Hardened Depth | 0.3-3.5mm can be choice |
| Chrome Thickness | 20-50µm can be choice |
| Chrome Hardness | min. 900 HV (0.1) |
| Straightness | <=Ø16 mm: max. 0.3 mm : 1000 mm > Ø16 mm: max. 0.2 mm : 1000 mm |
| Mechanical Properties | According to EN 10083-2 |
Quality Inspection and Testing
Packing and Delivery
Equipment Show
As one of the biggest honed tube piston rod manufacturers in China, we equipped with advanced production facilities and inspection facilities for honed pipe manufacturing and inspection. Below manufacturing machines for steel honed tubing and chrome plated hard bar
The hard chromium piston rods produced by our company come with more than JIS S45C material, where the rods first undergo precision milling and processing, and are then put through gard surface chromium treatment, allowing a surface precision level of f7, and a surface hardness reaching HV800 minimum and up, which not only help to improve wear resistance but also help to extend the life cycle of the rods, thus helping the customer save cost.
The corrosion resistances is tested in our own internal salt spray laboratory, and The rods surface heat treatment and hardness reaching HRC55°±2°, and at a hardened depth of between 0.5mm - 3mm, before the rods are put through precision milling and hard chromium treatment for a membrane thickness measuring 20 micron ± 10% to drastically improve the rod's wear resistance, and help to extend the life cycle of the rods.
1. Chrome Plated Steel Bars:
Our Chrome Plated Bars are produced from medium carbon cold-finished or hot rolled steel bars usually in 1045 grades. The bars are centerless ground, polished, and chrome plated to a minimum thickness of 0.0005", and 0.001" per side.
Chrome Plated bars are specifically designed to be used for most piston rod applications in hydraulic and pneumatic cylinders.
2. Induction Hardened Chrome Plated Bars:
Our Induction Hardened Chrome Plated Bars are produced by using advanced processing techniques usually on JIS S45C, SAE1045 or DIN CK45 steel rods, for surface removal, polishing, induction hardening, followed by hard chrome plating to a thickness minimum of 0.0005" or 0.001" per side. The finished product results in a superior impact resistant bar ideal for high quality piston rods capable of handling tough environments.
Applications:
Linear Motion Guides, Hydraulic cylinder rods
plastic injection molding machines, construction equipment, rubber molding machines, papermaking machines, printing machines, refrigeration equipment, foods and chemical machinery, loading equipment, fiber spinning equipment, textile machinery, agricultural equipment, automotives, shipbuilding and the like.
We sincerely hope there would be a chance for us to start business and build long term relationships may from an inquiry soon.
Induction Hardened Steel Piston Rod for Hydraulic Cylinder
Kelly
+8618661285080
exp@dhonedtube.com
https://honedtube.en.made-in-china.com
Description
Induction Hardened Steel Piston Rod for Hydraulic Cylinder
Hard chrome piston rods processed by more than ten processing, made by steel bar in material CK45, 20MnV6, 42CrMo4, SUS304, SUS316 etc.. Dia. Precision level of f7 tolerance, surface hardness min. HV900.
Chrome layer thickness 20-50micron can be choice, Salt spray test 60-90hours.
Induction hardened hardness HRC55±2, hardened depth 0.5-3.5mm can be choice.
>Equipment cover all production processing with stick QC system make better quality and keep improve.
>Huge material purchasing reduce production cost and final rate.
>Rich stock for normal size, order could be fast delivery in 7days.
>100% inspection and one-year quality guarantee to avoid any risk choice us.
CK45 Hard Chrome Rod
| Steel Grade | C45E (EN 10083) |
| Tolerance | ISO f7 |
| Length | 4000mm, 5800mm, 6000mm, 7500mm can be choice |
| Roughness | max. Ra0.20µm (statistic average: 0.05 - 0.15µm) |
| Hardness | HRC 15-25, HRC 20-30 (Based on different heat treatment) |
| Chrome Thickness | 20-50µm can be choice |
| Chrome Hardness | min. 900 HV (0.1) |
| Straightness | <=Ø16 mm: max. 0.3 mm : 1000 mm > Ø16 mm: max. 0.2 mm : 1000 mm |
| Mechanical Properties | According to EN 10083-2 |
CK45 Induction Hardened Chrome Rod
| Steel Grade | C45E (EN 10083) |
| Tolerance | ISO f7 |
| Length | 4000mm, 5800mm, 6000mm, 7500mm can be choice |
| Roughness | max. Ra0.20µm (statistic average: 0.05 - 0.15µm) |
| Hardness | HRC 55+/-2 |
| Hardened Depth | 0.3-3.5mm can be choice |
| Chrome Thickness | 20-50µm can be choice |
| Chrome Hardness | min. 900 HV (0.1) |
| Straightness | <=Ø16 mm: max. 0.3 mm : 1000 mm > Ø16 mm: max. 0.2 mm : 1000 mm |
| Mechanical Properties | According to EN 10083-2 |
Quality Inspection and Testing
Packing and Delivery
Equipment Show
As one of the biggest honed tube piston rod manufacturers in China, we equipped with advanced production facilities and inspection facilities for honed pipe manufacturing and inspection. Below manufacturing machines for steel honed tubing and chrome plated hard bar
The hard chromium piston rods produced by our company come with more than JIS S45C material, where the rods first undergo precision milling and processing, and are then put through gard surface chromium treatment, allowing a surface precision level of f7, and a surface hardness reaching HV800 minimum and up, which not only help to improve wear resistance but also help to extend the life cycle of the rods, thus helping the customer save cost.
The corrosion resistances is tested in our own internal salt spray laboratory, and The rods surface heat treatment and hardness reaching HRC55°±2°, and at a hardened depth of between 0.5mm - 3mm, before the rods are put through precision milling and hard chromium treatment for a membrane thickness measuring 20 micron ± 10% to drastically improve the rod's wear resistance, and help to extend the life cycle of the rods.
1. Chrome Plated Steel Bars:
Our Chrome Plated Bars are produced from medium carbon cold-finished or hot rolled steel bars usually in 1045 grades. The bars are centerless ground, polished, and chrome plated to a minimum thickness of 0.0005", and 0.001" per side.
Chrome Plated bars are specifically designed to be used for most piston rod applications in hydraulic and pneumatic cylinders.
2. Induction Hardened Chrome Plated Bars:
Our Induction Hardened Chrome Plated Bars are produced by using advanced processing techniques usually on JIS S45C, SAE1045 or DIN CK45 steel rods, for surface removal, polishing, induction hardening, followed by hard chrome plating to a thickness minimum of 0.0005" or 0.001" per side. The finished product results in a superior impact resistant bar ideal for high quality piston rods capable of handling tough environments.
Applications:
Linear Motion Guides, Hydraulic cylinder rods
plastic injection molding machines, construction equipment, rubber molding machines, papermaking machines, printing machines, refrigeration equipment, foods and chemical machinery, loading equipment, fiber spinning equipment, textile machinery, agricultural equipment, automotives, shipbuilding and the like.
We sincerely hope there would be a chance for us to start business and build long term relationships may from an inquiry soon.
Induction Hardened Steel Piston Rod for Hydraulic Cylinder
Kelly
+8618661285080
exp@dhonedtube.com
https://honedtube.en.made-in-china.com